Anodizing aluminum increases corrosion resistance, surface hardness and improves paint adhesion.

Aluminum parts are wired or placed into pinch racks and attached to a copper bar which helps conduct electricity. Only the surfaces that require anodize coating are exposed to the processing. All other surfaces or holes are protected using plugs or liquid maskant.

The parts are then lifted by hoist and lowered into the tanks. Parts are alkaline cleaned, etched and then deoxidized. This ensures that the parts are clean, free of foreign contaminants and ready for the anodize coating. Parts are then immersed into the anodize tank and charged with an electrical current, producing a layer of aluminum oxide on and into the aluminum surface.

Because of the electrical charge, if parts are racked or tied improperly, or the material type is identified improperly by the customer PO, the risk of the parts causing an arc and getting burned inside the tank is great. 3P takes great precaution to prevent damage to our customers’ parts.

Processed parts are inspected using a dualscope to measure coating thickness. Inspectors also visually check for corrosion, pitting or pockets in the material that could be cause for rejection. If the parts are deemed unacceptable by the inspector, parts are either written up for internal rework or returned to the customer for evaluation.

After processing and inspection, parts are moved to the next operation, typically paint or final inspection.

line 2  


3P offers 3 types of Anodize:

Chromic Acid Anodize (CAA) is the oldest, and first developed commercial anodize process. It generates a thin coating (0.5-.1 mils) on complex parts with tight tolerances. Chromic Acid Anodize is widely used wherever components have lap joints, recesses, crevices or other features that could trap the electrolyte solution (this solution will not substantially attack the material if entrapped during processing). Sealed CAA is used to improve paint adhesion. The color varies from light gray to dark gray depending on the material alloy, often it appears opaque.


Boric Sulfuric Acid Anodize (BSAA) was developed by the Boeing Company for use on non-critical fatigue parts (an alternative to CAA). The coating weight and color are the same, as are the characteristics of the electrolyte. BSAA is favored by environmental law due to the chrome-free chemistry; it is also more energy-efficient because it uses lower voltage. Paint adhesion is equal or superior to CAA.



Sulfuric Acid Anodize (SAA) produces a moderate coating up to 1mil for conventional coatings and up to 4 mils for hard anodize. Surfaces treated with sulfuric anodize are highly durable and can take on colors from gray to yellow depending on the alloy.

sulfuric sulfuric2
Customer Portal

To request access contact 3P customer service.
3P Approved for Boeing PS 20722

3P Processing is now approved for Boeing PS 20722!


Submit quotes via our RFQ Form or by sending us an email.

New Process Approvals

New process approvals for Beechcraft and Spirit


    Click here to view new approvals.

Virtual Tour

Tour our Facility!

Powered by:


3P Careers


For Current and Prospective Employees